PU Windscreen Sealant
Product feature:
1. High strength, high elasticity, excellent stickiness and cohesion made stickiness/airproof more flexible and resistent.
2. One-component, moisture curable, non-sagging, no dropping on stand surface, convenience construction.
3. No solvent, no corrosion to base materials, no pollution to the environment.
4. Excellent sealing, puncture resistance, good aging, oil and water resistance.
Applications
1. Elastic bondings for windshield and side glass of automobile repair.
Technical Data:
Test items Performance
Density: 1.35+/-0.05g/cm3
Touch dry time: 20~60 min
Curing in 24h: 3~5mm
Volatile content: < =4%
Shore A hardness: 55+/-5 Ao
Strength at break: >=5.0MPa
TENSILE-SHEAR STRENGTH: 2.0 MPa
Elongation at break: >=400%
Extrudability: 80ML/min
Application temperature: +5~+35
PU Windscreen Sealant
Product feature:
1. High strength, high elasticity, excellent stickiness and cohesion made stickiness/airproof more flexible and resistent.
2. One-component, moisture curable, non-sagging, no dropping on stand surface, convenience construction.
3. No solvent, no corrosion to base materials, no pollution to the environment.
4. Excellent sealing, puncture resistance, good aging, oil and water resistance.
Applications
1. Elastic bondings for windshield and side glass of automobile repair.
Technical Data:
Test items Performance
Density: 1.35+/-0.05g/cm3
Touch dry time: 20~60 min
Curing in 24h: 3~5mm
Volatile content: < =4%
Shore A hardness: 55+/-5 Ao
Strength at break: >=5.0MPa
TENSILE-SHEAR STRENGTH: 2.0 MPa
Elongation at break: >=400%
Extrudability: 80ML/min
Application temperature: +5~+35