| CAS No.: | Reference to MSDS |
|---|---|
| Bonding Function: | Windshield Sealant |
| Morphology: | Homogeneous Paste |
| Application: | Automobile, Windshield |
| Material: | Polyurethane |
| Main Agent Composition: | Polyurethane Elastomer |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Product Name: Primerless PU Adhesive Sealant for Windshield Repair
Company Name: Guangdong Pustar Adhesives & Sealants Co., Ltd.
Keywords: Windshield repair adhesive, Primerless adhesive sealant, Automotive glass sealant, PU adhesive for windshield repair, Adhesive sealant for auto glass, China auto glass sealant, Car windshield adhesive, Glass repair adhesive, Auto repair adhesive sealant, Bonding adhesive for glass, Polyurethane adhesive for windshield, Windscreen adhesive sealant, Adhesive and sealant for auto repair, Silicone sealant for windshield, Polyurethane adhesive sealant, China adhesive glue for auto glass, Auto glass repair adhesive, Primerless adhesive for windshield repair, Automotive sealant and adhesive, PU adhesive for auto repair, Windshield adhesive and sealant, China polyurethane adhesive sealant, Car glass repair adhesive, Adhesive glue for automotive glass, Auto glass sealant adhesive, China auto glass adhesive
Description: Our Primerless PU Adhesive Sealant for Windshield Repair is a high-quality product designed to provide strong bonding and sealing properties for automotive glass repair. It is easy to use and does not require a primer, making it convenient and efficient. Trust our adhesive sealant to ensure a reliable and durable repair for your windshield. Made by Guangdong Pustar Adhesives & Sealants Co., Ltd., a trusted supplier in China.
Technical date
|
Items |
Renz10 |
|
|
Scope |
Typical value |
|
|
Appearance |
Black, homogeneous paste |
/ |
|
Extrudability (ml/min) GB/T 13477.4 |
≥60 |
98 |
|
Sagging properties(mm) GB/T 13477.6 |
0 |
0 |
|
Tack free time(min) GB/T 13477.5 |
10~30 |
20 |
|
Curing speed(mm/d)HG/T 4363 |
≥3.0 |
3.5 |
|
Non-volatile contents (%)GB/T 2793 |
≥95 |
96 |
|
Shore A-hardness GB/T 531.1 |
55~65 |
60 |
|
Tensile strength(MPa) GB/T 528 |
≥4.5 |
5.2 |
|
Elongation at break(%) GB/T 528 |
≥400 |
450 |
|
Tear strength( N/mm) GB/T 529 |
≥8.0 |
9.4 |
|
Tensile-shear strength(MPa) GB/T 7124 |
≥2.5 |
3.0 |
|
Operating temperature(ºC) |
-40~90 |
|